| PA66 70G33L 美国杜邦公司 物性数据 |
 |
原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
24小时浸渍(23℃) |
ASTM D-570 |
0.5 |
% |
| 吸水率 |
饱和(23℃) |
ASTM D-570 |
4.6 |
% |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.35 |
--- |
| 机械性能 |
洛氏硬度M |
DAM |
ASTM D-785 |
M96 |
--- |
| 洛氏硬度M |
50%RH |
ASTM D-785 |
M90 |
--- |
| 洛氏硬度R |
DAM |
ASTM D-785 |
R122 |
--- |
| 洛氏硬度R |
50%RH |
ASTM D-785 |
R118 |
--- |
| 泰伯磨耗量 |
50%RH |
--- |
36 |
cycles |
| 拉伸强度 |
23℃,DAM |
ASTM D-638 |
151.6 |
MPa |
| 拉伸强度 |
23℃,50%RH |
ASTM D-638 |
110.3 |
MPa |
| 断裂伸长率 |
23℃,DAM |
ASTM D-638 |
3 |
% |
| 断裂伸长率 |
23℃,50%RH |
ASTM D-638 |
4 |
% |
| 挤剪强度 |
23℃,DAM |
ASTM D-732 |
72 |
MPa |
| 挠曲模量 |
23℃,DAM |
ASTM D-790 |
6895 |
MPa |
| 挠曲模量 |
23℃,50%RH |
ASTM D-790 |
5516 |
MPa |
| 挠曲强度 |
23℃,DAM |
ASTM D-790 |
228 |
MPa |
| 埃佐冲击强度 |
23℃,DAM |
ASTM D-256 |
128 |
j/m |
| 埃佐冲击强度 |
23℃,50%RH |
ASTM D-256 |
128 |
j/m |
| 电气性能 |
介电强度 |
DAM |
ASTM D-149 |
630 |
volts/mil |
| 介电强度 |
100%RH |
ASTM D-149 |
255 |
volts/mil |
| 体积电阻率 |
100%RH |
ASTM D-257 |
109 |
ohm-cm |
| 损耗因数 |
DAM@106Hz赫 |
ASTM D-150 |
0.02 |
--- |
| 体积电阻率 |
DAM |
ASTM D-257 |
1014 |
ohm-cm |
| 介电强度 |
(分步法)DAM |
ASTM D-149 |
510 |
volts/mil |
| 介电常数 |
DAM@103Hz赫 |
ASTM D-150 |
4.2 |
--- |
| 介电常数 |
DAM@106Hz赫 |
ASTM D-150 |
3.4 |
--- |
| 损耗因数 |
DAM@103Hz赫 |
ASTM D-150 |
0.02 |
--- |
| 热 性 能 |
熔点 |
50%RH |
ASTM D-789 |
255 |
℃ |
| 线性热膨胀系数 |
--- |
ASTM D-696 |
1.8×10-5 |
m/m/℃ |
| 熔点 |
DAM |
ASTM D-789 |
255 |
℃ |
| 热畸变温度 |
1.8MPa |
ASTM D-648 |
246 |
℃ |
|